Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 132 GPa Show Material materials with Elastic modulus of 132 GPa | |
Elongation | 23.0 °C | 40 % Show Material materials with Elongation of 40 % | |
Hardness, Vickers | 23.0 °C | 40 - 70 [-] Show Material materials with Hardness, Vickers of 40 - 70 [-] | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa Show Material materials with Shear modulus of 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 23.0 °C | 220 MPa Show Material materials with Tensile strength of 220 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.68E-5 - 1.77E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.68E-5 - 1.77E-5 1/K | |
100.0 °C | 1.68E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.68E-5 1/K | ||
200.0 °C | 1.73E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.73E-5 1/K | ||
300.0 °C | 1.77E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K | ||
Melting point | 1083 °C Show Material materials with Melting point of 1083 °C | ||
Specific heat capacity | 23.0 °C | 377 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal conductivity | 23.0 °C | 293 - 364 W/(m·K) Show Material materials with Thermal conductivity of 293 - 364 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 4.10E+7 - 5.20E+7 S/m Show Material materials with Electrical conductivity of 4.10E+7 - 5.20E+7 S/m |
Electrical resistivity | 23.0 °C | 1.92E-8 - 2.44E-8 Ω·m Show Material materials with Electrical resistivity of 1.92E-8 - 2.44E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Copper | 99.9 % Show Material materials with Copper of 99.9 % |
Other | total 0.03. excluded Ag, Ni, P |
Phosphorus | 0.02 - 0.04 % Show Material materials with Phosphorus of 0.02 - 0.04 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing : very good, soft brazing: very good | |
| Workability | Cold forming degree between anneals: max. 95 %, general (condition): very good | |