General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.8 g/cm³ Show Material materials with Density of 8.8 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Dicke |
Mechanical
Property | Temperature | Value |
---|---|---|
Bending angle 90° | 20.0 °C | 0 °/t Show Material materials with Bending angle 90° of 0 °/t |
Elastic modulus | 20.0 °C | 125 GPa Show Material materials with Elastic modulus of 125 GPa |
Elongation A50 | 20.0 °C | 8 - 10 % Show Material materials with Elongation A50 of 8 - 10 % |
Hardness, Vickers | 20.0 °C | 100 - 120 [-] Show Material materials with Hardness, Vickers of 100 - 120 [-] |
Tensile strength | 20.0 °C | 340 - 390 MPa Show Material materials with Tensile strength of 340 - 390 MPa |
Yield strength Rp0.2 | 20.0 °C | 240 MPa Show Material materials with Yield strength Rp0.2 of 240 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.63E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.63E-5 1/K |
100.0 °C | 1.63E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.63E-5 1/K | |
Melting point | 1084 - 1089 °C Show Material materials with Melting point of 1084 - 1089 °C | |
Thermal conductivity | 20.0 °C | 200 - 260 W/(m·K) Show Material materials with Thermal conductivity of 200 - 260 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.70E+7 - 3.80E+7 S/m Show Material materials with Electrical conductivity of 1.70E+7 - 3.80E+7 S/m |
Electrical resistivity | 20.0 °C | 2.63E-8 - 5.88E-8 Ω·m Show Material materials with Electrical resistivity of 2.63E-8 - 5.88E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Iron | 2.1 - 2.6 % Show Material materials with Iron of 2.1 - 2.6 % |
Lead | 0.03 % Show Material materials with Lead of 0.03 % |
Other | Rest Cu, total 0.2 |
Phosphorus | 0.02 - 0.15 % Show Material materials with Phosphorus of 0.02 - 0.15 % |
Zinc | 0.05 - 0.2 % Show Material materials with Zinc of 0.05 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 90 %, general (condition): good |