General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Dimension
| Property | Value |
|---|---|
Dimensions | Durchmesser |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elongation | 20.0 °C | 25 % Show Material materials with Elongation of 25 % |
Elongation A100 | 20.0 °C | 20 % Show Material materials with Elongation A100 of 20 % |
Hardness, Brinell | 20.0 °C | 65 - 95 [-] Show Material materials with Hardness, Brinell of 65 - 95 [-] |
Hardness, Vickers | 20.0 °C | 70 - 100 [-] Show Material materials with Hardness, Vickers of 70 - 100 [-] |
Tensile strength | 20.0 °C | 250 MPa Show Material materials with Tensile strength of 250 MPa |
Yield strength Rp0.2 | 20.0 °C | 140 MPa Show Material materials with Yield strength Rp0.2 of 140 MPa |
Thermal
| Property | Value |
|---|---|
Melting point | 1038 - 1082 °C Show Material materials with Melting point of 1038 - 1082 °C |
Chemical properties
| Property | Value |
|---|---|
Nickel | 0.8 - 1.2 % Show Material materials with Nickel of 0.8 - 1.2 % |
Other | Rest Cu, total 0.1 |
Phosphorus | 0.15 - 0.25 % Show Material materials with Phosphorus of 0.15 - 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing : good to medium, soft brazing: good | |
| Workability | Cold forming degree between anneals: max. 75 % (lösungsgeglüht), general (condition): good (solution annealed) | |