Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Elongation | 23.0 °C | 7 % Show Material materials with Elongation of 7 % | |
Elongation A100 | 23.0 °C | 3 % Show Material materials with Elongation A100 of 3 % | |
Hardness, Brinell | 23.0 °C | 90 [-] Show Material materials with Hardness, Brinell of 90 [-] | |
Hardness, Vickers | 23.0 °C | 90 [-] Show Material materials with Hardness, Vickers of 90 [-] | |
Tensile strength | 23.0 °C | 250 MPa Show Material materials with Tensile strength of 250 MPa | |
Yield strength Rp0.2 | 23.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper High Copper Alloy |
Melting point | 855 - 1090 °C Show Material materials with Melting point of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Chemical properties
| Property | Value |
|---|---|
Lead | 0.7 - 1.5 % Show Material materials with Lead of 0.7 - 1.5 % |
Other | Rest Cu, total 0.1 |
Phosphorus | 0 - 0.01 % Show Material materials with Phosphorus of 0 - 0.01 % |