General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Dicke |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 125 GPa Show Material materials with Elastic modulus of 125 GPa |
Elongation | 20.0 °C | 42 % Show Material materials with Elongation of 42 % |
Elongation A50 | 20.0 °C | 33 % Show Material materials with Elongation A50 of 33 % |
Hardness, Vickers | 20.0 °C | 40 - 65 [-] Show Material materials with Hardness, Vickers of 40 - 65 [-] |
Tensile strength | 20.0 °C | 220 - 260 MPa Show Material materials with Tensile strength of 220 - 260 MPa |
Yield strength Rp0.2 | 20.0 °C | 140 MPa Show Material materials with Yield strength Rp0.2 of 140 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.77E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K |
100.0 °C | 1.77E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K | |
Melting point | 1081 °C Show Material materials with Melting point of 1081 °C | |
Thermal conductivity | 20.0 °C | 385 W/(m·K) Show Material materials with Thermal conductivity of 385 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 5.20E+7 S/m Show Material materials with Electrical conductivity of 5.20E+7 S/m |
Electrical resistivity | 20.0 °C | 1.92E-8 Ω·m Show Material materials with Electrical resistivity of 1.92E-8 Ω·m |
Chemical properties
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good to good, soft brazing: very good to good | |
Workability | Cold forming degree between anneals: max. 95 %, general (condition): very good |