SN 211605 Grade CW306G

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.7 - 8.7 g/cm³

Show Material materials with Density of 7.7 - 8.7 g/cm³

Typical for Leaded Phosphor Bronze

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

110 - 130 GPa

Show Material materials with Elastic modulus of 110 - 130 GPa

Typical for Leaded Phosphor Bronze

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Leaded Phosphor Bronze

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-5 - 1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.5E-5 - 1.9E-5 1/K

Typical for Leaded Phosphor Bronze

Specific heat capacity

23.0 °C

380 J/(kg·K)

Show Material materials with Specific heat capacity of 380 J/(kg·K)

Typical for Leaded Phosphor Bronze

Chemical properties

PropertyValue

Aluminium

8.5 - 11 %

Show Material materials with Aluminium of 8.5 - 11 %

Iron

2 - 4 %

Show Material materials with Iron of 2 - 4 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Manganese

1.5 - 3.5 %

Show Material materials with Manganese of 1.5 - 3.5 %

Nickel

1 %

Show Material materials with Nickel of 1 %

Other

Rest Cu, total 0.3

Zinc

0.5 %

Show Material materials with Zinc of 0.5 %