General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Dicke |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 120 GPa Show Material materials with Elastic modulus of 120 GPa |
Elongation | 20.0 °C | 50 % Show Material materials with Elongation of 50 % |
Elongation A50 | 20.0 °C | 40 % Show Material materials with Elongation A50 of 40 % |
Hardness, Vickers | 20.0 °C | 70 - 100 [-] Show Material materials with Hardness, Vickers of 70 - 100 [-] |
Tensile strength | 20.0 °C | 290 - 390 MPa Show Material materials with Tensile strength of 290 - 390 MPa |
Yield strength Rp0.2 | 20.0 °C | 190 MPa Show Material materials with Yield strength Rp0.2 of 190 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.82E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.82E-5 1/K |
100.0 °C | 1.82E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.82E-5 1/K | |
Melting point | 950 - 1070 °C Show Material materials with Melting point of 950 - 1070 °C | |
Thermal conductivity | 20.0 °C | 90 W/(m·K) Show Material materials with Thermal conductivity of 90 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.10E+7 S/m Show Material materials with Electrical conductivity of 1.10E+7 S/m |
Electrical resistivity | 20.0 °C | 9.09E-8 Ω·m Show Material materials with Electrical resistivity of 9.09E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Iron | 0.1 % Show Material materials with Iron of 0.1 % |
Lead | 0.02 % Show Material materials with Lead of 0.02 % |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % |
Other | Rest Cu, total 0.2 |
Phosphorus | 0.01 - 0.4 % Show Material materials with Phosphorus of 0.01 - 0.4 % |
Tin | 3.5 - 4.5 % Show Material materials with Tin of 3.5 - 4.5 % |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 80 %, general (condition): very good |