General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.8 g/cm³ Show Material materials with Density of 8.8 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Dicke |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 120 GPa Show Material materials with Elastic modulus of 120 GPa |
Elongation | 20.0 °C | 30 % Show Material materials with Elongation of 30 % |
Elongation A50 | 20.0 °C | 25 % Show Material materials with Elongation A50 of 25 % |
Hardness, Vickers | 20.0 °C | 80 - 110 [-] Show Material materials with Hardness, Vickers of 80 - 110 [-] |
Tensile strength | 20.0 °C | 320 - 380 MPa Show Material materials with Tensile strength of 320 - 380 MPa |
Yield strength Rp0.2 | 20.0 °C | 230 MPa Show Material materials with Yield strength Rp0.2 of 230 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.8E-5 1/K |
100.0 °C | 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.8E-5 1/K | |
Melting point | 1010 - 1030 °C Show Material materials with Melting point of 1010 - 1030 °C | |
Thermal conductivity | 20.0 °C | 120 W/(m·K) Show Material materials with Thermal conductivity of 120 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.20E+7 S/m Show Material materials with Electrical conductivity of 1.20E+7 S/m |
Electrical resistivity | 20.0 °C | 8.33E-8 Ω·m Show Material materials with Electrical resistivity of 8.33E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Iron | 0.1 % Show Material materials with Iron of 0.1 % |
Lead | 0.1 % Show Material materials with Lead of 0.1 % |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % |
Other | Rest Cu, total 0.2 |
Phosphorus | 0.2 % Show Material materials with Phosphorus of 0.2 % |
Tin | 1.5 - 3.5 % Show Material materials with Tin of 1.5 - 3.5 % |
Zinc | 7.5 - 10 % Show Material materials with Zinc of 7.5 - 10 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 90 %, general (condition): very good |