General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.8 g/cm³ Show Material materials with Density of 8.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 110 - 130 GPa Show Material materials with Elastic modulus of 110 - 130 GPa | Typical for Leaded Phosphor Bronze |
Elongation | 23.0 °C | 10 % Show Material materials with Elongation of 10 % | |
Elongation A100 | 23.0 °C | 6 % Show Material materials with Elongation A100 of 6 % | |
Hardness, Brinell | 23.0 °C | 150 [-] Show Material materials with Hardness, Brinell of 150 [-] | |
Hardness, Vickers | 23.0 °C | 150 [-] Show Material materials with Hardness, Vickers of 150 [-] | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Leaded Phosphor Bronze |
Tensile strength | 23.0 °C | 450 MPa Show Material materials with Tensile strength of 450 MPa | |
Yield strength Rp0.2 | 23.0 °C | 350 MPa Show Material materials with Yield strength Rp0.2 of 350 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 - 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.5E-5 - 1.9E-5 1/K | Typical for Leaded Phosphor Bronze |
Melting point | 930 - 1060 °C Show Material materials with Melting point of 930 - 1060 °C | ||
Specific heat capacity | 23.0 °C | 380 J/(kg·K) Show Material materials with Specific heat capacity of 380 J/(kg·K) | Typical for Leaded Phosphor Bronze |
Chemical properties
Property | Value |
---|---|
Iron | 0.1 % Show Material materials with Iron of 0.1 % |
Lead | 0.5 - 1.5 % Show Material materials with Lead of 0.5 - 1.5 % |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % |
Other | Rest Cu, total 0.2 |
Phosphorus | 0.01 - 0.4 % Show Material materials with Phosphorus of 0.01 - 0.4 % |
Tin | 3.5 - 5.5 % Show Material materials with Tin of 3.5 - 5.5 % |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : good to medium, soft brazing: very good to good | |
Workability | Cold forming degree between anneals: max. 75 %, general (condition): good to medium |