Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.5 g/cm³ Show Material materials with Density of 8.5 g/cm³ |
Dimension
| Property | Value |
|---|---|
Dimensions | Dicke |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 115 GPa Show Material materials with Elastic modulus of 115 GPa |
Elongation | 20.0 °C | 50 % Show Material materials with Elongation of 50 % |
Elongation A50 | 20.0 °C | 40 % Show Material materials with Elongation A50 of 40 % |
Hardness, Vickers | 20.0 °C | 55 - 90 [-] Show Material materials with Hardness, Vickers of 55 - 90 [-] |
Tensile strength | 20.0 °C | 270 - 350 MPa Show Material materials with Tensile strength of 270 - 350 MPa |
Yield strength Rp0.2 | 20.0 °C | 160 MPa Show Material materials with Yield strength Rp0.2 of 160 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.97E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.97E-5 1/K |
100.0 °C | 1.97E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.97E-5 1/K | |
Melting point | 910 - 965 °C Show Material materials with Melting point of 910 - 965 °C | |
Thermal conductivity | 20.0 °C | 126 W/(m·K) Show Material materials with Thermal conductivity of 126 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.70E+7 S/m Show Material materials with Electrical conductivity of 1.70E+7 S/m |
Electrical resistivity | 20.0 °C | 5.88E-8 Ω·m Show Material materials with Electrical resistivity of 5.88E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Copper | 69 - 71 % Show Material materials with Copper of 69 - 71 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Other | Rest Zn, total 0.1 |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing : very good, soft brazing: very good | |
| Workability | Cold forming degree between anneals: max. 90 %, general (condition): very good | |