General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.4 g/cm³ Show Material materials with Density of 8.4 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Dicke |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 110 GPa Show Material materials with Elastic modulus of 110 GPa |
Elongation | 20.0 °C | 48 % Show Material materials with Elongation of 48 % |
Elongation A50 | 20.0 °C | 38 % Show Material materials with Elongation A50 of 38 % |
Hardness, Vickers | 20.0 °C | 55 - 95 [-] Show Material materials with Hardness, Vickers of 55 - 95 [-] |
Tensile strength | 20.0 °C | 300 - 370 MPa Show Material materials with Tensile strength of 300 - 370 MPa |
Yield strength Rp0.2 | 20.0 °C | 180 MPa Show Material materials with Yield strength Rp0.2 of 180 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 20.0 °C | 2.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.02E-5 1/K |
100.0 °C | 2.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.02E-5 1/K | |
Melting point | 902 - 920 °C Show Material materials with Melting point of 902 - 920 °C | |
Thermal conductivity | 20.0 °C | 121 W/(m·K) Show Material materials with Thermal conductivity of 121 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.55E+7 S/m Show Material materials with Electrical conductivity of 1.55E+7 S/m |
Electrical resistivity | 20.0 °C | 6.45E-8 Ω·m Show Material materials with Electrical resistivity of 6.45E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.05 % Show Material materials with Aluminium of 0.05 % |
Copper | 62 - 64 % Show Material materials with Copper of 62 - 64 % |
Iron | 0.1 % Show Material materials with Iron of 0.1 % |
Lead | 0.1 % Show Material materials with Lead of 0.1 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Other | Rest Zn, total 0.1 |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 65 %, general (condition): very good |