CEN/TS 13388 Grade CW602N R280

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

23.0 °C

8.4 g/cm³

Show Material materials with Density of 8.4 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

100 - 125 GPa

Show Material materials with Elastic modulus of 100 - 125 GPa

Typical for Wrought Copper Brass

Elongation

23.0 °C

30 %

Show Material materials with Elongation of 30 %

Hardness, Brinell

23.0 °C

80 [-]

Show Material materials with Hardness, Brinell of 80 [-]

Hardness, Vickers

23.0 °C

80 [-]

Show Material materials with Hardness, Vickers of 80 [-]

Shear modulus

23.0 °C

40 GPa

Show Material materials with Shear modulus of 40 GPa

Typical for Wrought Copper Brass

Tensile strength

23.0 °C

280 MPa

Show Material materials with Tensile strength of 280 MPa

Yield strength Rp0.2

23.0 °C

120 MPa

Show Material materials with Yield strength Rp0.2 of 120 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

885 - 910 °C

Show Material materials with Melting point of 885 - 910 °C

Specific heat capacity

23.0 °C

371 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K)

Typical for Wrought Copper Brass

Thermal conductivity

23.0 °C

100 - 234 W/(m·K)

Show Material materials with Thermal conductivity of 100 - 234 W/(m·K)

Typical for Wrought Copper Brass

Chemical properties

PropertyValue

Aluminium

0.05 %

Show Material materials with Aluminium of 0.05 %

Arsenic

0.02 - 0.15 %

Show Material materials with Arsenic of 0.02 - 0.15 %

Copper

61 - 63 %

Show Material materials with Copper of 61 - 63 %

Iron

0.1 %

Show Material materials with Iron of 0.1 %

Lead

1.7 - 2.8 %

Show Material materials with Lead of 1.7 - 2.8 %

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

Nickel

0.3 %

Show Material materials with Nickel of 0.3 %

Other

Rest Zn, total 0.2

Tin

0.1 %

Show Material materials with Tin of 0.1 %

Technological properties

Property
Brazing

hard brazing : good, soft brazing: very good

Workability

Cold forming degree between anneals: max. 45 %, general (condition): good to medium