1200 H111 Non-Heat Treatable Al Wrought Alloy

.XLSX
.PDF
Save

Description

Very good corrosion resistance and workability. Very ductile in annealed condition.

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.69 g/cm³ at 20 °C

Dimension

Thickness t

0.2 - 3 mm

Mechanical

Bending angle 180° θ180

0 °/t at 20 °C

Bending angle 90° θ90

0 °/t at 20 °C

Elastic modulus E

70 GPa at 20 °C

Elongation A50 A50

19 % at 20 °C

Hardness, HBW HBW

23 [-] at 20 °C

Shear modulus G

26.5 GPa at 20 °C

Tensile strength Rm

75 - 105 MPa at 20 °C

Yield strength YS

25 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.4E-5 1/K at 100 °C

20-100°C

Thermal conductivity λ

138 W/(m·K) at 20 °C

Electrical

Electrical resistivity ρel

4.9E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Fe

1 %

Si + Fe

Si

1 %

Si + Fe

Other

0.15 %

Zn

0.1 %

Cu

0.05 %

More

Technological properties

Anodizing

Very Good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels; Electronic devices: Housing of devices; Heat exchangers: Fins; Cable wrapping: Electric cable wrapping; Insulation; Solar: Solar collectors; Semi-rigid and corrugated: Smooth wall

Brazing

Excellent

Corrosion properties

Very Good

Workability

Excellent

This material data has been provided by Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.