General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 2.71 g/cm³ Show Supplier Material materials with Density of 2.71 g/cm³ |
Dimension
Property | Value |
---|---|
Thickness | 0.2 - 1 mm Show Supplier Material materials with Thickness of 0.2 - 1 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Bending angle 180° | 23.0 °C | 2.5 °/t Show Supplier Material materials with Bending angle 180° of 2.5 °/t |
Elastic modulus | 23.0 °C | 69 GPa Show Supplier Material materials with Elastic modulus of 69 GPa |
Elongation A50 | 23.0 °C | 4 % Show Supplier Material materials with Elongation A50 of 4 % |
Hardness, HBW | 23.0 °C | 47 [-] Show Supplier Material materials with Hardness, HBW of 47 [-] |
Shear modulus | 23.0 °C | 26 GPa Show Supplier Material materials with Shear modulus of 26 GPa |
Tensile strength | 23.0 °C | 150 - 200 MPa Show Supplier Material materials with Tensile strength of 150 - 200 MPa |
Yield strength | 23.0 °C | 120 MPa Show Supplier Material materials with Yield strength of 120 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 172 W/(m·K) Show Supplier Material materials with Thermal conductivity of 172 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 3.8E-8 Ω·m Show Supplier Material materials with Electrical resistivity of 3.8E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Chromium | 0.2 % Show Supplier Material materials with Chromium of 0.2 % |
Copper | 0.3 % Show Supplier Material materials with Copper of 0.3 % |
Iron | 0.7 % Show Supplier Material materials with Iron of 0.7 % |
Magnesium | 0.2 - 0.8 % Show Supplier Material materials with Magnesium of 0.2 - 0.8 % |
Manganese | 0.3 - 0.8 % Show Supplier Material materials with Manganese of 0.3 - 0.8 % |
Silicon | 0.6 % Show Supplier Material materials with Silicon of 0.6 % |
Zinc | 0.4 % Show Supplier Material materials with Zinc of 0.4 % |
Technological properties
Property | ||
---|---|---|
Anodizing | Good | |
Application areas | Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Heat exchangers: Fins; Closures: Short cups; Semi-rigid and corrugated: Pet food | |
Brazing | Good | |
Corrosion properties | Very Good | |
Surface Finish | Mill finish | |
Welding | Very Good | |
Workability | Very Good |