5049 H34 Non-Heat Treatable Al Wrought Alloy

.XLSX
.PDF
Save

Description

Universal work hardening alloy offering medium strength, very good formability, very good corrosion resistance, and good durability.

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.7 g/cm³ at 20 °C

Dimension

Thickness t

0.2 - 6 mm

Mechanical

Bending angle 180° θ180

2.5 °/t at 20 °C

Bending angle 90° θ90

1 °/t at 20 °C

Elastic modulus E

70 GPa at 20 °C

Elongation A50 A50

6 - 8 % at 20 °C

Hardness, HBW HBW

70 [-] at 20 °C

Shear modulus G

26.5 GPa at 20 °C

Tensile strength Rm

240 - 280 MPa at 20 °C

Yield strength YS

160 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.4E-5 1/K at 100 °C

20-100°C

Thermal conductivity λ

147 W/(m·K) at 20 °C

Electrical

Electrical resistivity ρel

4.4E-8 - 5E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Mg

1.6 - 2.5 %

Fe

0.5 %

Mn

0.5 - 1.1 %

Si

0.4 %

Cr

0.3 %

More

Technological properties

Anodizing

Excellent (anodizing quality)

Application areas

Components: General trasportation

Brazing

Poor

Corrosion properties

Excellent

Workability

Very Good (in O temper)

This material data has been provided by Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.