5050 H32 Non-Heat Treatable Al Wrought Alloy

.XLSX
.PDF
Save

Description

Very good corrosion resistance and workability. Very ductile in annealed condition.

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.69 g/cm³ at 20 °C

Dimension

Thickness t

0.5 - 3 mm

Mechanical

Bending angle 180° θ180

1 °/t at 20 °C

Bending angle 90° θ90

0.5 °/t at 20 °C

Elastic modulus E

68.6 GPa at 20 °C

Elongation A50 A50

4 - 10 % at 20 °C

Hardness, HBW HBW

47 [-] at 20 °C

Shear modulus G

26.5 GPa at 20 °C

Tensile strength Rm

155 - 195 MPa at 20 °C

Yield strength YS

110 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.4E-5 1/K at 100 °C

20-100°C

Thermal conductivity λ

192 W/(m·K) at 20 °C

Electrical

Electrical resistivity ρel

3.4E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Mg

1.1 - 1.8 %

Fe

0.7 %

Si

0.4 %

Zn

0.25 %

Cu

0.2 %

More

Technological properties

Anodizing

Very Good (anodizing quality)

Application areas

Roofing: Single sheet, Sheets for composites/ sandwich Panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels, Decoration; Anodizing quality; Tubes: Industrial tubes, Pipes; Food can: Body, Lids

Brazing

Good

Corrosion properties

Excellent

General machinability

Fair

Workability

Very Good

This material data has been provided by Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.