General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 2.66 g/cm³ Show Supplier Material materials with Density of 2.66 g/cm³ |
Dimension
Property | Value |
---|---|
Thickness | 1.5 - 12.5 mm Show Supplier Material materials with Thickness of 1.5 - 12.5 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Bending angle 180° | 23.0 °C | 1.5 °/t Show Supplier Material materials with Bending angle 180° of 1.5 °/t |
Bending angle 90° | 23.0 °C | 2.5 °/t Show Supplier Material materials with Bending angle 90° of 2.5 °/t |
Elastic modulus | 23.0 °C | 71 GPa Show Supplier Material materials with Elastic modulus of 71 GPa |
Elongation A50 | 23.0 °C | 11 - 16 % Show Supplier Material materials with Elongation A50 of 11 - 16 % |
Hardness, HBW | 23.0 °C | 75 [-] Show Supplier Material materials with Hardness, HBW of 75 [-] |
Shear modulus | 23.0 °C | 27.6 GPa Show Supplier Material materials with Shear modulus of 27.6 GPa |
Tensile strength | 23.0 °C | 270 - 350 MPa Show Supplier Material materials with Tensile strength of 270 - 350 MPa |
Yield strength | 23.0 °C | 115 - 125 MPa Show Supplier Material materials with Yield strength of 115 - 125 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 117 W/(m·K) Show Supplier Material materials with Thermal conductivity of 117 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 5.9E-8 Ω·m Show Supplier Material materials with Electrical resistivity of 5.9E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Chromium | 0.05 - 0.25 % Show Supplier Material materials with Chromium of 0.05 - 0.25 % |
Copper | 0.1 % Show Supplier Material materials with Copper of 0.1 % |
Iron | 0.4 % Show Supplier Material materials with Iron of 0.4 % |
Magnesium | 4 - 4.9 % Show Supplier Material materials with Magnesium of 4 - 4.9 % |
Manganese | 0.4 - 1 % Show Supplier Material materials with Manganese of 0.4 - 1 % |
Other | 0.05 - 0.15 % Show Supplier Material materials with Other of 0.05 - 0.15 % |
Silicon | 0.4 % Show Supplier Material materials with Silicon of 0.4 % |
Titanium | 0.15 % Show Supplier Material materials with Titanium of 0.15 % |
Zinc | 0.25 % Show Supplier Material materials with Zinc of 0.25 % |
Technological properties
Property | ||
---|---|---|
Application areas | Vessels: Pressure, Cryogenics; Tubes: Industrial tubes, Pipes; Wind energy: Nacelle coverings, rotor hub, stairs; Components: Access hatches, Spoilers, Fuel and oil tanks, General tranportation | |
Brazing | Brazing is not recommended | |
Corrosion properties | Excellent | |
Welding | Good | |
Workability | Good (in O temper) |