General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 2.66 g/cm³ Show Supplier Material materials with Density of 2.66 g/cm³ |
Dimension
Property | Value |
---|---|
Thickness | 0.2 - 4 mm Show Supplier Material materials with Thickness of 0.2 - 4 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 71 GPa Show Supplier Material materials with Elastic modulus of 71 GPa |
Elongation A50 | 23.0 °C | 1 - 2 % Show Supplier Material materials with Elongation A50 of 1 - 2 % |
Hardness, HBW | 23.0 °C | 98 [-] Show Supplier Material materials with Hardness, HBW of 98 [-] |
Shear modulus | 23.0 °C | 27 GPa Show Supplier Material materials with Shear modulus of 27 GPa |
Tensile strength | 23.0 °C | 325 - 385 MPa Show Supplier Material materials with Tensile strength of 325 - 385 MPa |
Yield strength | 23.0 °C | 270 MPa Show Supplier Material materials with Yield strength of 270 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 126 W/(m·K) Show Supplier Material materials with Thermal conductivity of 126 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 5.6E-8 Ω·m Show Supplier Material materials with Electrical resistivity of 5.6E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Chromium | 0.05 - 0.25 % Show Supplier Material materials with Chromium of 0.05 - 0.25 % |
Copper | 0.1 % Show Supplier Material materials with Copper of 0.1 % |
Iron | 0.5 % Show Supplier Material materials with Iron of 0.5 % |
Magnesium | 3.5 - 4.5 % Show Supplier Material materials with Magnesium of 3.5 - 4.5 % |
Manganese | 0.2 - 0.7 % Show Supplier Material materials with Manganese of 0.2 - 0.7 % |
Other | 0.05 - 0.15 % Show Supplier Material materials with Other of 0.05 - 0.15 % |
Silicon | 0.4 % Show Supplier Material materials with Silicon of 0.4 % |
Titanium | 0.15 % Show Supplier Material materials with Titanium of 0.15 % |
Zinc | 0.25 % Show Supplier Material materials with Zinc of 0.25 % |
Technological properties
Property | ||
---|---|---|
Anodizing | Excellent (anodizing quality) | |
Application areas | Vessels: Pressure, Cryogenics; Components: Access hatches, Spoilers, General tranportation | |
Corrosion properties | Excellent | |
Welding | Good | |
Workability | Good (in O temper) |