8006 H24 Non-Heat Treatable Al Wrought Alloy

.XLSX
.PDF
Save

Description

High strength when compared to 1xxx in foil app. Alloy 8006 can be welded, adhesive bonded, and formed easily. It offers a useful combination of strength and ductility at room temperature while retaining its strength at elevated temperatures.

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.74 g/cm³ at 20 °C

Dimension

Thickness t

0.06 - 0.2 mm

Mechanical

Elastic modulus E

70 GPa at 20 °C

Elongation A50 A50

5 % at 20 °C

Shear modulus G

25 GPa at 20 °C

Tensile strength Rm

110 - 170 MPa at 20 °C

Yield strength YS

90 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.4E-5 1/K at 100 °C

20-100°C

Thermal conductivity λ

190 - 210 W/(m·K) at 20 °C

Electrical

Electrical resistivity ρel

3.1E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Fe

1.2 - 2 %

Si

0.4 %

Cu

0.3 %

Mn

0.3 - 1 %

Mg

0.1 %

More

Technological properties

Anodizing

Limited

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels; Electronic devices: Housing of devices; Heat exchangers: Fins, Heat exchangers, General applications; Tubes: Industrial tubes, Flexible tubes, Pipes; Insulation; Semi-rigid and corrugated: Pet food, Smooth wall; Components: Automotive fins, Heat exchangers

Corrosion properties

Limited

Workability

Very Good

This material data has been provided by Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.