Pebax® C 63C73 SP 01

Alternative and trade names
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® C 63C73 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant.

Pebax® C is the new route explored to design cost-efficient components while preserving Pebax® resin key features. The percentage of renewable carbon according to ASTM D6866 (calculated) is 51%.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Value	Condition	Testing Standard
Bio-based content	51 % Show Supplier Material materials with Bio-based content of 51 %
Density	1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³	dry	ISO 1183

Mechanical

Property	Value	Condition	Testing Standard	Comment
Hardness, Shore D	61 [-] Show Supplier Material materials with Hardness, Shore D of 61 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	No Break at 23°C	dry	ISO 179/1eA
Impact strength, Charpy unnotched	No Break at 23 and -30°C	dry	ISO 179/1eU
Yield strength	43 MPa Show Supplier Material materials with Yield strength of 43 MPa	cond.	ISO 527-1/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	218 °C Show Supplier Material materials with Melting point of 218 °C	dry	ISO 11357-1/-3	10°C/min

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Shrinkage	0.9 % Show Supplier Material materials with Shrinkage of 0.9 %	dry	ISO 294-4
	1.3 % Show Supplier Material materials with Shrinkage of 1.3 %	dry	ISO 294-4	Transverse

Technological properties

Property

Application areas

Footwear - Outsoles

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max): 250°C / 270°C / 290°C.

Typical mold temperature: 30-60°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-8 hours at 60-70°C.