General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 1.48 - 1.52 g/cm³ Show Supplier Material materials with Density of 1.48 - 1.52 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 8.1 - 8.9 GPa Show Supplier Material materials with Elastic modulus of 8.1 - 8.9 GPa | ISO 527-2 |
Elongation | 20.0 °C | 2 - 4 % Show Supplier Material materials with Elongation of 2 - 4 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 20.0 °C | 5 - 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 - 9 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 20.0 °C | 50 - 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 50 - 70 kJ/m² | ISO 179/1eA |
Tensile strength | 20.0 °C | 90 - 110 MPa Show Supplier Material materials with Tensile strength of 90 - 110 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 20.0 °C | 28 - 32 % Show Supplier Material materials with Ash content of 28 - 32 % | DIN EN 3451 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt volume-flow rate | 12 - 18 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 - 18 cm³/10min | ISO 1133, 250°C/2,16Kg |
Technological properties
Property | ||
---|---|---|
Application areas | Connectors, E&E Cases, Covers, Frames | |
Fillers | 30% Glass Fiber | |
Processing methods | Pre-drying 4 hours/100-120°C |