General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 1.32 - 1.36 g/cm³ Show Supplier Material materials with Density of 1.32 - 1.36 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 7 - 8 GPa Show Supplier Material materials with Elastic modulus of 7 - 8 GPa | ISO 527-2 |
Elongation | 20.0 °C | 4.7 - 5.3 % Show Supplier Material materials with Elongation of 4.7 - 5.3 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 20.0 °C | 7 - 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 - 11 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 20.0 °C | 40 - 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 40 - 60 kJ/m² | ISO 179/1eA |
Tensile strength | 20.0 °C | 110 - 130 MPa Show Supplier Material materials with Tensile strength of 110 - 130 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value |
---|---|---|
Ash content | 20.0 °C | 28 - 32 % Show Supplier Material materials with Ash content of 28 - 32 % |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt volume-flow rate | 40 - 80 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 40 - 80 cm³/10min | ISO 1133, 275°C/5Kg |
Technological properties
Property | ||
---|---|---|
Application areas | Chair cross as well as different parts for chairs, Ventilation inlet systems for tractors, excavators, wheel loaders, buses etc., Cable ducts, Components in automotive engineering | |
Fillers | 30% Glass Fiber | |
Processing methods | Pre-drying 2-4 hours/83°C |