Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 1.1 - 1.14 g/cm³ Show Supplier Material materials with Density of 1.1 - 1.14 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 2 - 2.4 GPa Show Supplier Material materials with Elastic modulus of 2 - 2.4 GPa | ISO 527-2 | ||
Elongation | 20.0 °C | 22 - 24 % Show Supplier Material materials with Elongation of 22 - 24 % | ISO 527-1/-2 | ||
Impact strength, Charpy notched | 20.0 °C | 16 - 24 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 - 24 kJ/m² | ISO 179/1eA | ||
Tensile strength | 20.0 °C | 40 - 50 MPa Show Supplier Material materials with Tensile strength of 40 - 50 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 20.0 °C | 2 % Show Supplier Material materials with Ash content of 2 % | Maximum |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt volume-flow rate | 25 - 35 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 25 - 35 cm³/10min | ISO 1133, 260°C/5Kg |
Technological properties
Property | ||
---|---|---|
Application areas | Car trim parts, Interior cases | |
Fillers | 65% Talc | |
Processing methods | Pre-drying 4 hours/95-110°C |