Properties
General
Dimension
| Property | Value |
|---|---|
Thickness | 6 - 575 mm Show Supplier Material materials with Thickness of 6 - 575 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 69 GPa Show Supplier Material materials with Elastic modulus of 69 GPa |
Elongation | 23.0 °C | 20 % Show Supplier Material materials with Elongation of 20 % |
Hardness, HBW | 23.0 °C | 20 [-] Show Supplier Material materials with Hardness, HBW of 20 [-] |
Shear modulus | 23.0 °C | 25.9 GPa Show Supplier Material materials with Shear modulus of 25.9 GPa |
Tensile strength | 23.0 °C | 65 MPa Show Supplier Material materials with Tensile strength of 65 MPa |
Yield strength | 23.0 °C | 28 MPa Show Supplier Material materials with Yield strength of 28 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.35E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.35E-5 1/K | Mean values between 20°C and the mentioned temperature |
200.0 °C | 2.44E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.44E-5 1/K | Mean values between 20°C and the mentioned temperature | |
300.0 °C | 2.54E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.54E-5 1/K | Mean values between 20°C and the mentioned temperature | |
Specific heat capacity | 23.0 °C | 900 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 900 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 210 - 220 W/(m·K) Show Supplier Material materials with Thermal conductivity of 210 - 220 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 3.40E+7 - 3.60E+7 S/m Show Supplier Material materials with Electrical conductivity of 3.40E+7 - 3.60E+7 S/m |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Aluminium | Balance | ||
Copper | 0.05 % Show Supplier Material materials with Copper of 0.05 % | ||
Iron | 0.4 % Show Supplier Material materials with Iron of 0.4 % | ||
Magnesium | 0.05 % Show Supplier Material materials with Magnesium of 0.05 % | ||
Manganese | 0.05 % Show Supplier Material materials with Manganese of 0.05 % | ||
Other | 0.03 % Show Supplier Material materials with Other of 0.03 % | Single | |
Silicon | 0.25 % Show Supplier Material materials with Silicon of 0.25 % | ||
Titanium | 0.05 % Show Supplier Material materials with Titanium of 0.05 % | ||
Zinc | 0.07 % Show Supplier Material materials with Zinc of 0.07 % | ||
Technological properties
| Property | ||
|---|---|---|
| Anodizing | very good | |
| Application areas | Electronics industry; Semiconductor industry; Panelling in machine construction and plant construction; Parts with a decorative surface; Automotive parts; Food industry | |
| Corrosion properties | good | |
| Dimensional stability | very good | |
| General machinability | very good | |
| Soldering general | very good | |
| Welding | Gas: good, WIG: good | |