Zirconia Toughened Alumina ZTA-C

Alternative and trade names
Zirconia Toughened Alumina

Want to keep this datasheet? Save it now in your required format

Description

With this mixture of ceramics, a small amount of zirconium dioxide is added to the aluminum oxide which significantly improves the hardness and stability and simultaneously increases the toughness. It has following features:

Hardness

Resistance to pressure

Resistance to thermal shock

Reistance to temperature

Flexural Strenth

This material data has been provided by Bosch Advanced Ceramics.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	4.1 g/cm³ Show Supplier Material materials with Density of 4.1 g/cm³
Surface roughness		3.6 μm Show Supplier Material materials with Surface roughness of 3.6 μm	Rz*

Mechanical

Property	Temperature	Value	Comment
Compressive strength	23.0 °C	2600 MPa Show Supplier Material materials with Compressive strength of 2600 MPa
Elastic modulus	23.0 °C	360 GPa Show Supplier Material materials with Elastic modulus of 360 GPa
Flexural strength	23.0 °C	600 MPa Show Supplier Material materials with Flexural strength of 600 MPa	4-point bending flexural test
Hardness, Vickers	23.0 °C	1733 [-] Show Supplier Material materials with Hardness, Vickers of 1733 [-]	converted from GPa
Plane-Strain Fracture Toughnes	23.0 °C	5 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 5 MPa·√m

Thermal

Property	Temperature	Value
Coefficient of thermal expansion	23.0 °C	9E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-6 1/K
Thermal conductivity	23.0 °C	25 W/(m·K) Show Supplier Material materials with Thermal conductivity of 25 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	20.0 °C	1.00E+14 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+14 Ω·m
	600.0 °C	1000000 Ω·m Show Supplier Material materials with Electrical resistivity of 1000000 Ω·m

Technological properties

Property

Application areas

Cutting materials for machine

Valves, gear wheels

Sensors

For highest mechanical loads

Other

*depending on the processing status of the injection molding or pressing tool

Processing history

Ceramic Injection Molding (CIM)