Properties
General
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Density | 25 °C | 1.11 g/cm³ Show Supplier Material materials with Density of 1.11 g/cm³ | ISO 1183-1 | |
Low volatile organic compounds emissions | 23 °C | 10 μg/g Show Supplier Material materials with Low volatile organic compounds emissions of 10 μg/g | VDA 278 | max. |
Total volatile organic compounds emissions | 23 °C | 15 μgC/g Show Supplier Material materials with Total volatile organic compounds emissions of 15 μgC/g | VDA 277 | max. |
Volatile organic compounds emissions | 23 °C | 10 μg/g Show Supplier Material materials with Volatile organic compounds emissions of 10 μg/g | VDA 278 | max. |
Water absorption | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62 | 23 °C | 50 % r.h., Equilibrium | |
0.7 % Show Supplier Material materials with Water absorption of 0.7 % | ISO 62 | Water at 23 °C, Saturation |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527-1/2 | 1 mm/min | |
Elongation | 45 % Show Supplier Material materials with Elongation of 45 % | ISO 527-1/2 | 50 mm/min | |
Elongation at yield | 4.5 % Show Supplier Material materials with Elongation at yield of 4.5 % | ISO 527-1/2 | 50 mm/min | |
Flexural modulus | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | |
Flexural strength | 85 MPa Show Supplier Material materials with Flexural strength of 85 MPa | ISO 178 | 2 mm/min | |
Impact strength, Izod notched | -40 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 30 kJ/m² | ISO 180-1A | |
-30 °C | 39 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 39 kJ/m² | ISO 180-1A | ||
23 °C | 51 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 51 kJ/m² | ISO 180-1A | ||
Yield strength | 53 MPa Show Supplier Material materials with Yield strength of 53 MPa | ISO 527-1/2 | 50 mm/min |
Thermal
| Property | Value | Testing Standard | Pressure | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 8e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
8.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.2e-05 1/K | ISO 11359-1/2 | 23 to 55°C, Transverse | |||||
Heat deflection temperature | 101 °C Show Supplier Material materials with Heat deflection temperature of 101 °C | ISO 75-1/2 | 1.8 MPa | ||||
120 °C Show Supplier Material materials with Heat deflection temperature of 120 °C | ISO 75-1/2 | 0.45 MPa | |||||
Vicat softening temperature | 118 °C Show Supplier Material materials with Vicat softening temperature of 118 °C | ISO 306 | B50 | 50°C/h | ||||
120 °C Show Supplier Material materials with Vicat softening temperature of 120 °C | ISO 306 | B120 | 120°C/h | |||||
Flammability | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (150x105x1 mm): < 80 mm/min according to ISO 3795 | ||||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Melt volume-flow rate | 21 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 21 cm³/10min | ISO 1133 | 260°C/5Kg |
Shrinkage | 0.65 - 0.75 % Show Supplier Material materials with Shrinkage of 0.65 - 0.75 % | ISO 294-4 | 60x60x2 mm |
0.65 - 0.75 % Show Supplier Material materials with Shrinkage of 0.65 - 0.75 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Chemical composition | Thermoplastic polymer blend based on polycarbonate (PC) and acrylonitrile-butadiene-styrene (ABS). | |
| Color | White to slightly yellowish. | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 260 ºC according to ISO 294 Injection molding-mold temperature: 80 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |