Mechanical
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elastic modulus | 2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa | ISO 527-1/2 | 1 mm/min | |
Elongation | 15 % Show Supplier Material materials with Elongation of 15 % | ISO 527-1/2 | min. | 50 mm/min | |
Elongation at yield | 2.5 % Show Supplier Material materials with Elongation at yield of 2.5 % | ISO 527-1/2 | 50 mm/min | |
Flexural modulus | 2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min | |
Flexural strength | 67 MPa Show Supplier Material materials with Flexural strength of 67 MPa | ISO 178 | 2 mm/min | |
Hardness, Ball Indentation | 95 MPa Show Supplier Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | -30 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179-1eA | |
23 °C | 22 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 22 kJ/m² | ISO 179-1eA | ||
Impact strength, Charpy unnotched | -30 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179-1eU | |
23 °C | 140 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 140 kJ/m² | ISO 179-1eU | ||
Impact strength, Izod notched | -30 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180-1A | |
23 °C | 21 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 21 kJ/m² | ISO 180-1A | ||
Yield strength | 43 MPa Show Supplier Material materials with Yield strength of 43 MPa | ISO 527-1/2 | 50 mm/min |
Thermal
Property | Value | Testing Standard | Pressure | Comment |
---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2.0 mm | |
Heat deflection temperature | 95 °C Show Supplier Material materials with Heat deflection temperature of 95 °C | ISO 75-1/2 | 1.8 MPa | |
100 °C Show Supplier Material materials with Heat deflection temperature of 100 °C | ISO 75-1/2 | 0.45 MPa | ||
Vicat softening temperature | 100 °C Show Supplier Material materials with Vicat softening temperature of 100 °C | ISO 306 | 50 N | 50°C/h |
Electrical
Property | Value | Testing Standard | Frequency | Comment |
---|---|---|---|---|
Comparative tracking index | 575 V Show Supplier Material materials with Comparative tracking index of 575 V | IEC 60112 | Solution A | |
Dielectric constant | 2.9 [-] Show Supplier Material materials with Dielectric constant of 2.9 [-] | IEC 60250 | 1MHz | |
3.1 [-] Show Supplier Material materials with Dielectric constant of 3.1 [-] | IEC 60250 | 100Hz | ||
Dielectric strength | 34 kV/mm Show Supplier Material materials with Dielectric strength of 34 kV/mm | IEC 60243-1 | 1 mm | |
Dissipation factor | 0.005 [-] Show Supplier Material materials with Dissipation factor of 0.005 [-] | IEC 60250 | 100Hz | |
0.009 [-] Show Supplier Material materials with Dissipation factor of 0.009 [-] | IEC 60250 | 1MHz | ||
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | |||
Volume resistivity | 1e+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+17 Ω·cm | IEC 60093 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt volume-flow rate | 5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min | ISO 1133 | 220°C/10Kg |
Shrinkage | 0.5 - 0.7 % Show Supplier Material materials with Shrinkage of 0.5 - 0.7 % | ISO 294-4 | 60x60x2 mm |
0.5 - 0.7 % Show Supplier Material materials with Shrinkage of 0.5 - 0.7 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
Property | ||
---|---|---|
Certifications | UL Certificate | |
Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 |