Properties
General
| Property | Temperature | Value | Testing Standard |
|---|---|---|---|
Density | 25 °C | 1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³ | ISO 1183-1 |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 2.1 GPa Show Supplier Material materials with Elastic modulus of 2.1 GPa | ISO 527-1/2 | 1 mm/min | |
Elongation | 30 % Show Supplier Material materials with Elongation of 30 % | ISO 527-1/2 | 50 mm/min | |
Elongation at yield | 4 % Show Supplier Material materials with Elongation at yield of 4 % | ISO 527-1/2 | 50 mm/min | |
Flexural modulus | 2.1 GPa Show Supplier Material materials with Flexural modulus of 2.1 GPa | ISO 527-1/2 | 2 mm/min | |
Flexural strength | 73 MPa Show Supplier Material materials with Flexural strength of 73 MPa | ISO 178 | 2 mm/min | |
Hardness, Ball Indentation | 103 MPa Show Supplier Material materials with Hardness, Ball Indentation of 103 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | -30 °C | 24 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 24 kJ/m² | ISO 179-1eA | |
23 °C | 50 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 50 kJ/m² | ISO 179-1eA | ||
Impact strength, Izod notched | -30 °C | 26 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 26 kJ/m² | ISO 180-1A | |
23 °C | 58 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 58 kJ/m² | ISO 180-1A | ||
Yield strength | 44 MPa Show Supplier Material materials with Yield strength of 44 MPa | ISO 527-1/2 | 50 mm/min |
Thermal
| Property | Value | Testing Standard | Pressure | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 9.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9.5e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
Heat deflection temperature | 95 °C Show Supplier Material materials with Heat deflection temperature of 95 °C | ISO 75-1/2 | 1.8 MPa | ||||
113 °C Show Supplier Material materials with Heat deflection temperature of 113 °C | ISO 75-1/2 | 0.45 MPa | |||||
Vicat softening temperature | 113 °C Show Supplier Material materials with Vicat softening temperature of 113 °C | ISO 306 | B50 | 50°C/h | ||||
Flammability | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (200x105x2 mm): < 50 mm/min according to ISO 3795 | ||||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Melt volume-flow rate | 26 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 26 cm³/10min | ISO 1133 | 260°C/5Kg |
Shrinkage | 0.55 - 0.65 % Show Supplier Material materials with Shrinkage of 0.55 - 0.65 % | ISO 294-4 | 60x60x2 mm |
0.55 - 0.65 % Show Supplier Material materials with Shrinkage of 0.55 - 0.65 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Chemical composition | Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide). | |
| Color | White to slightly yellowish. | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |