General
Property | Temperature | Value | Testing Standard |
---|---|---|---|
Density | 25 °C | 1.03 g/cm³ Show Supplier Material materials with Density of 1.03 g/cm³ | ISO 1183-1 |
Mechanical
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elastic modulus | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527-1/2 | 1 mm/min | |
Elongation | 19 % Show Supplier Material materials with Elongation of 19 % | ISO 527-1/2 | 50 mm/min | |
Flexural modulus | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 527-1/2 | 2 mm/min | |
Flexural strength | 71 MPa Show Supplier Material materials with Flexural strength of 71 MPa | ISO 178 | 2 mm/min | |
Hardness, Ball Indentation | 105 MPa Show Supplier Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | 23 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179-1eA | |
Impact strength, Izod notched | -30 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180-1A | |
23 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180-1A | ||
Yield strength | 45 MPa Show Supplier Material materials with Yield strength of 45 MPa | ISO 527-1/2 | 50 mm/min |
Thermal
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 9.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9.2e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
Heat deflection temperature | 101 °C Show Supplier Material materials with Heat deflection temperature of 101 °C | ISO 75-1/2 | 1.8 MPa | ||||
107 °C Show Supplier Material materials with Heat deflection temperature of 107 °C | ISO 75-1/2 | 0.45 MPa | |||||
Vicat softening temperature | 108 °C Show Supplier Material materials with Vicat softening temperature of 108 °C | ISO 306 | B50 | 50°C/h | ||||
110 °C Show Supplier Material materials with Vicat softening temperature of 110 °C | ISO 306 | B120 | 120°C/h | |||||
Flammability | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (200x105x2 mm): < 55 mm/min according to ISO 3795 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt volume-flow rate | 12 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | 220°C/10Kg |
Shrinkage | 0.6 - 0.7 % Show Supplier Material materials with Shrinkage of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm |
0.6 - 0.7 % Show Supplier Material materials with Shrinkage of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
Property | ||
---|---|---|
Certifications | UL Certificate | |
Chemical composition | Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI). | |
Color | White to slightly yellowish. | |
Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 |