Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 5.75 g/cm³ Show Supplier Material materials with Density of 5.75 g/cm³ | typical properties |
Loss on Ignition | 0.3 % Show Supplier Material materials with Loss on Ignition of 0.3 % | |
Water content | 0.2 % Show Supplier Material materials with Water content of 0.2 % |
Mechanical
| Property | Value | Comment |
|---|---|---|
Hardness, Vickers | 1275.0 [-] Show Supplier Material materials with Hardness, Vickers of 1275.0 [-] | typical properties |
Plane-Strain Fracture Toughnes | 6.8 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 6.8 MPa·√m | typical properties |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Shrinkage | 19.0 % Show Supplier Material materials with Shrinkage of 19.0 % | sintering, typical properties |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 0.02 Show Supplier Material materials with Aluminium of 0.02 | max. Al₂O₃ |
Calcium | 0.02 % Show Supplier Material materials with Calcium of 0.02 % | CaO |
Iron | 0.02 Show Supplier Material materials with Iron of 0.02 | max. Fe₂O₃ |
Magnesium | 3.2 % Show Supplier Material materials with Magnesium of 3.2 % | MgO |
Silicon | 0.2 Show Supplier Material materials with Silicon of 0.2 | max. SiO₂ |
Titanium | 0.1 Show Supplier Material materials with Titanium of 0.1 | max. TiO₂ |
Zirconium | 96 % Show Supplier Material materials with Zirconium of 96 % | ZrO₂+HfO₂ |
Technological properties
| Property | ||
|---|---|---|
| Application areas | GNPGraystar’s Mg-PSZ is best used for textile ceramic pieces, high temperature steam valves, wire drawing dies, pulley cones, thermocouple protection tubes, oxygen probe protection tubes, etc. | |
| Color | Yellow | |
| Processing history | Sintering temperature: 1700°C | |