Fused Magnesium-Aluminate Spinel FS33

Want to keep this datasheet? Save it now in your required format

Description

GNPGraystar’s Fused MagnesiumAluminate Spinel is made of high purity raw materials in electric arc furnaces. The maximum amount of spinel crystals is achieved by using pure raw materials and electric arc furnaces. The product has a high thermal shock resistance and slag corrosion resistance, and good refractoriness.

This material data has been provided by GNPGraystar Specialty Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValue

Density

3.5 g/cm³

Show Supplier Material materials with Density of 3.5 g/cm³

Porosity

7.0 %

Show Supplier Material materials with Porosity of 7.0 %

Chemical properties

PropertyValueComment

Aluminium

64.5 - 67.5 %

Show Supplier Material materials with Aluminium of 64.5 - 67.5 %

Al₂O₃

Calcium

0.65

Show Supplier Material materials with Calcium of 0.65

max. CaO

Iron

0.3

Show Supplier Material materials with Iron of 0.3

max. Fe₂O₃

Magnesium

31.5 - 34.5 %

Show Supplier Material materials with Magnesium of 31.5 - 34.5 %

MgO

Silicon

0.4

Show Supplier Material materials with Silicon of 0.4

max. SiO₂

Sodium

0.25

Show Supplier Material materials with Sodium of 0.25

max. Na₂O

Technological properties

Property
Application areas

GNPGraystar’s FS33 is used in the production of refractory materials used for the sinter and transit zones of rotary furnaces in the cement industry, for the arches of electric arc furnaces, for the refractory lining of highfrequency furnaces, and various kinds of torpedo ladles and other ladles used in the steel industry.