Nickel 99.98% Rod & Wire S-Annealed

Alternative and trade names
N02270, 2.4050, N02200, N02201, 2.4060, 2.4061, 2.4066, 2.4068, N02205, Pure Nickel
Want to keep this datasheet? Save it now in your required format

Description

Nickel with highest degree of purity with the following features:


  • Very low levels of carbon (20 ppm) and sulfur (2 ppm) which tend to segregate at grain boundries resulting in hot shortening
  • Cleanliness, absence of non-metallic inclusions as Al, Ti or Si oxides
  • Low electrical resistivity at 20°C
  • High thermal conductivity at 20°C
  • Excellent formability
  • Low softening temperature (350°C)
  • Low recrystallization temperature (350°C)
  • Improved oxidation resistance: development of tightly adherent one-layer oxide scale instead of a two-layer costumary one, which tends to flake off due to mismatch in thermal expansion.
  • Equivalent Materials

    This material data has been provided by Hpulcas GmbH.

    "Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
    All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
    Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

    Ashby charts

    Properties

    Dimension

    PropertyValue

    Dimensions

    Rod: Diameter: up to 4.7 mm, Length: up to 2500 mm - Wire: Diameter: 0.2-1.6 mm ; various dimensions can be also customized

    Mechanical

    PropertyTemperatureValueComment

    Elastic modulus

    23.0 °C

    196 GPa

    Show Supplier Material materials with Elastic modulus of 196 GPa

    Hardness, Vickers

    23.0 °C

    65 [-]

    Show Supplier Material materials with Hardness, Vickers of 65 [-]

    max.

    Thermal

    PropertyTemperatureValue

    Recrystallization temperature

    350 °C

    Show Supplier Material materials with Recrystallization temperature of 350 °C

    Thermal conductivity

    23.0 °C

    90.9 - 91 W/(m·K)

    Show Supplier Material materials with Thermal conductivity of 90.9 - 91 W/(m·K)

    Electrical

    PropertyTemperatureValue

    Electrical resistivity

    23.0 °C

    7.1E-8 Ω·m

    Show Supplier Material materials with Electrical resistivity of 7.1E-8 Ω·m

    Chemical properties

    PropertyValue

    Carbon

    2E-3 %

    Show Supplier Material materials with Carbon of 2E-3 %

    Nickel

    99.98 %

    Show Supplier Material materials with Nickel of 99.98 %

    Sulfur

    2E-4 %

    Show Supplier Material materials with Sulfur of 2E-4 %

    Technological properties

    Property
    Application areas

    Wire: Sputter Targets, evaporation pellets, regulator coil in glow plugs of diesel engines; litz wire for current conduction under elevated temperatures and in aggressive environments, Pre material for thin wire manfacturing, Ni wire mesh, Thermal Spraying, Coating layer for corrosion protection from alkalis; salt spray; molten salt and reduciing chemicals; coating layer for high temperature resistance; corrosion protection at high temperatures; coating layer for membrane walls of power plants

    Heat Treatment

    Soft Annealed

    Processing history

    For producing wire, the 6 mm hot rolled thick plates are cut into 6 mm wide sticks. The sticks are frontally welded. Afterwards the raw wire can be treated in the same way as hot rolled wire produced by melt metallurgy. accordingly, the wire is drawn to the desired dimensions through cold drawing and intermediate annealing.

    Surface Finish

    Blank/Bare/bright surface