Water absorption cwater

4.17 % at 20 °C

neat resin: 54h, boiling water (neat resin)


Flexural strength σbend

162 MPa at 20 °C

(neat resin)

Fracture toughness KIC

1.88 MPa·√m at 20 °C

(neat resin)

Strain energy release GIC

1340 J/m² at 20 °C

(neat resin)

Tensile strength Rm

94 MPa at 20 °C


Glass transition temperature Tg

154 - 175 °C

wet and dry glass transition temperature respectively (neat resin)

Max service temperature Tmax

120 °C

in loaded parts

Technological properties


The key features and benefits are: high mechanical performance, possibility of application in loaded parts at service temperatures up to 120°C, less stringent requirements for working staff, glass transition temperature 154°C, out of autoclave processing.

This material data has been provided by ITECMA.