Reinforced with 68% Carbon Fibers
Density ρ
1.6 g/cm³ at 20 °C
Elastic modulus E
250 GPa at 20 °C
Elongation A
1.7 % at 20 °C
Poisson's ratio ν
0.25 [-] at 20 °C
Shear strength τ
40 MPa at 20 °C
Tensile strength Rm
4900 MPa at 20 °C
Processing methods
The production process is formed by laminating hot-pressed carbon fiber prepreg.
This material data has been provided by Jinjiuyi Carbon Fiber Team.