General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Supplier Material materials with Density of 8.9 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Available size round products (mm): 1-35 |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 165 GPa Show Supplier Material materials with Elastic modulus of 165 GPa |
Elongation | 23.0 °C | 10 % Show Supplier Material materials with Elongation of 10 % |
Hardness, Brinell | 23.0 °C | 137 - 180 [-] Show Supplier Material materials with Hardness, Brinell of 137 - 180 [-] |
Hardness, Rockwell C | 23.0 °C | 0 - 10 [-] Show Supplier Material materials with Hardness, Rockwell C of 0 - 10 [-] |
Hardness, Vickers | 23.0 °C | 140 - 180 [-] Show Supplier Material materials with Hardness, Vickers of 140 - 180 [-] |
Tensile strength | 23.0 °C | 500 - 650 MPa Show Supplier Material materials with Tensile strength of 500 - 650 MPa |
Yield strength | 23.0 °C | 300 MPa Show Supplier Material materials with Yield strength of 300 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.72E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.72E-5 1/K | for 20-200°C |
Thermal conductivity | 23.0 °C | 22.5 W/(m·K) Show Supplier Material materials with Thermal conductivity of 22.5 W/(m·K) | for 20-200°C |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 2.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 2.00E+6 S/m |
Magnetic
Property | Temperature | Value |
---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] Show Supplier Material materials with Relative magnetic permeability of 1 [-] |
Technological properties
Property | ||
---|---|---|
Application areas | Summary of typical applications: Mechanical parts in very demanding environments | |
Corrosion properties | Corrosion resistance rating: 5 out of 5 | |
General machinability | Machinability: 40 % | |
Processing history | Condition: H11 |