General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ASTM D792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 58.26 GPa Show Supplier Material materials with Elastic modulus of 58.26 GPa | ASTM D790 |
Elongation | 23.0 °C | 1 % Show Supplier Material materials with Elongation of 1 % | ASTM D638 |
Flexural modulus | 23.0 °C | 17.33 GPa Show Supplier Material materials with Flexural modulus of 17.33 GPa | ASTM D790 |
Flexural strength | 23.0 °C | 427 MPa Show Supplier Material materials with Flexural strength of 427 MPa | ASTM D790 |
Impact strength, Izod notched, ASTM | 23.0 °C | 224 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 224 J/m | ASTM D256 |
Tensile strength | 23.0 °C | 289 MPa Show Supplier Material materials with Tensile strength of 289 MPa | ASTM D638 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 252 °C | ASTM D648 | |
Flammability | HB ASTM D635, for 1.5mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.1 - 0.3 % Show Supplier Material materials with Shrinkage of 0.1 - 0.3 % | ASTM D955, (1/8 in (3.2 mm)section) |
Technological properties
Property | ||
---|---|---|
Application areas | For the main wing of the aircraft, Duck wing, Stable wing nacelle and other aerospace fields | |
Color | Black | |
Fillers | 40% Long Carbon Fiber | |
Processing methods | Injection Moulding. Injection Pressure 69 - 124 MPa, Melt Temperature 277 - 299 °C, Mould temperature 90 - 120 °C, Pre-drying 4 hrs @ 90 - 110°C, Moisture Content 0.2%, Dew Point -18°C |