Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 8.36 g/cm³ Show Supplier Material materials with Density of 8.36 g/cm³ at 23.0 °C | 23.0 °C |
Dimension
| Property | Value |
|---|---|
Thickness | 0.05 - 0.9 mm Show Supplier Material materials with Thickness of 0.05 - 0.9 mm |
Width | 1.27 - 406.5 mm Show Supplier Material materials with Width of 1.27 - 406.5 mm |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Bendability 90°, bw | 0 [-] Show Supplier Material materials with Bendability 90°, bw of 0 [-] at 23.0 °C | 23.0 °C | for strip with 0.20mm and thinner. |
Bendability 90°, gw | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] at 23.0 °C | 23.0 °C | for strip with 0.20mm and thinner. |
Elastic modulus | 131 GPa Show Supplier Material materials with Elastic modulus of 131 GPa at 23.0 °C | 23.0 °C | |
Elongation | 14 % Show Supplier Material materials with Elongation of 14 % at 23.0 °C | 23.0 °C | min., for strip thicker than 0.10 mm |
Tensile strength | 820 MPa Show Supplier Material materials with Tensile strength of 820 MPa at 23.0 °C | 23.0 °C | min. |
Yield strength Rp0.2 | 95 - 115 MPa Show Supplier Material materials with Yield strength Rp0.2 of 95 - 115 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 870 °C Show Supplier Material materials with Melting point of 870 °C | |
Thermal conductivity | 105 W/(m·K) Show Supplier Material materials with Thermal conductivity of 105 W/(m·K) at 23.0 °C | 23.0 °C |
Electrical
| Property | Value | Temperature |
|---|---|---|
Electrical resistivity | 6.2E-8 - 1.01E-7 Ω·m Show Supplier Material materials with Electrical resistivity of 6.2E-8 - 1.01E-7 Ω·m at 23.0 °C | 23.0 °C |
Specific Electrical conductivity | 17 - 28 % IACS Show Supplier Material materials with Specific Electrical conductivity of 17 - 28 % IACS |
Chemical properties
| Property | ||
|---|---|---|
Beryllium | 1.8 - 2.2 % | |
Cobalt | 0.2 % | min. Nickel + Cobalt |
Copper | Balance | |
Iron | 0.6 % | max., Nickel + Cobalt + Iron |
Nickel | 0.2 % | min. Nickel + Cobalt |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include high reliability spring contacts for battery contacts, audio jack contacts, and board to board contacts. | |