General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.15 g/cm³ Show Material materials with Density of 1.15 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 0.06 GPa Show Material materials with Elastic modulus of 0.06 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 900 % Show Material materials with Elongation of 900 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.06 GPa Show Material materials with Flexural modulus of 0.06 GPa | ISO 178 |
Hardness, Shore D | 23.0 °C | 38 [-] Show Material materials with Hardness, Shore D of 38 [-] | max., ISO 7619-1 |
Impact strength, Charpy notched | -40.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy notched of 100 kJ/m² | No Break @ 23,-6°C, ISO 179/1eA |
Impact strength, Izod unnotched | -40.0 °C | 68 kJ/m² Show Material materials with Impact strength, Izod unnotched of 68 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.5 [-] Show Material materials with Poisson's ratio of 0.5 [-] | |
Tensile strength | 23.0 °C | 24 MPa Show Material materials with Tensile strength of 24 MPa | ISO 527-1/-2 |
Thermal
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9.5 g/10min Show Material materials with Melt mass-flow rate of 9.5 g/10min | ISO 1133 | 190°C/2.16kg | |
Shrinkage | 23.0 °C | 0.2 % Show Material materials with Shrinkage of 0.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Material materials with Shrinkage, transverse of 0.2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 180°C, Mold Temperature Optimum: 35°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |