General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 2.5 % Show Material materials with Water absorption of 2.5 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.11 GPa Show Material materials with Elastic modulus of 0.11 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 400 % Show Material materials with Elongation of 400 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.11 GPa Show Material materials with Flexural modulus of 0.11 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 48 [-] Show Material materials with Hardness, Shore D of 48 [-] | max., ISO 7619-1 | ||
Impact strength, Charpy notched | -40.0 °C | 120 kJ/m² Show Material materials with Impact strength, Charpy notched of 120 kJ/m² | No Break @ 23,-6°C, ISO 179/1eU | ||
Shear modulus | 23.0 °C | 0.04 GPa Show Material materials with Shear modulus of 0.04 GPa | ISO 6721 | ||
Tear strength | 23.0 °C | 100 kN/m Show Material materials with Tear strength of 100 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 90 kN/m Show Material materials with Tear strength, transverse of 90 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 17 MPa Show Material materials with Tensile strength of 17 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA | ||||
Impact strength, Izod unnotched | No Break @ 23,-40°C, ISO180/1A |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -66 °C Show Material materials with Brittleness temperature of -66 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 2.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.9E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.9E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | -45 °C Show Material materials with Glass transition temperature of -45 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 60 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 60 °C | ISO 75-1/-2 | |||
Melting point | 208 °C Show Material materials with Melting point of 208 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2100 J/(kg·K) Show Material materials with Specific heat capacity of 2100 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 165 °C Show Material materials with Vicat softening temperature of 165 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Ignition Temperature, 80mil: 675 °C, Glow Wire Temperature, No Flame, 80mil: 650 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 33 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 4.7 [-] Show Material materials with Dielectric constant, 1MHz of 4.7 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 11 cm³/10min Show Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.5 % Show Material materials with Shrinkage of 1.5 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.2 % Show Material materials with Shrinkage, transverse of 1.2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |