General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.26 g/cm³ Show Material materials with Density of 1.26 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.3 % Show Material materials with Water absorption of 0.3 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 0.55 GPa Show Material materials with Elastic modulus of 0.55 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 530 % Show Material materials with Elongation of 530 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 23 % Show Material materials with Elongation at yield of 23 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 0.55 GPa Show Material materials with Flexural modulus of 0.55 GPa | ISO 178 |
Hardness, Shore D | 23.0 °C | 68 [-] Show Material materials with Hardness, Shore D of 68 [-] | max., ISO 7619-1 |
Impact strength, Charpy notched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
-6.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | |
23.0 °C | 36 kJ/m² Show Material materials with Impact strength, Charpy notched of 36 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A |
23.0 °C | 38 kJ/m² Show Material materials with Impact strength, Izod unnotched of 38 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.47 [-] Show Material materials with Poisson's ratio of 0.47 [-] | |
Shear modulus | 23.0 °C | 0.28 GPa Show Material materials with Shear modulus of 0.28 GPa | ISO 6721 |
Tear strength | 23.0 °C | 182 kN/m Show Material materials with Tear strength of 182 kN/m | ISO 34-1 |
Tear strength, transverse | 23.0 °C | 172 kN/m Show Material materials with Tear strength, transverse of 172 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ISO 527-1/-2 |
Yield strength | 23.0 °C | 27 MPa Show Material materials with Yield strength of 27 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -97 °C Show Material materials with Brittleness temperature of -97 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 25 °C Show Material materials with Glass transition temperature of 25 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 100 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 100 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |||
Melting point | 218 °C Show Material materials with Melting point of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 85 °C Show Material materials with Relative temperature index, electrical of 85 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | 60mil | |||
Specific heat capacity | 23.0 °C | 2150 J/(kg·K) Show Material materials with Specific heat capacity of 2150 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 205 °C Show Material materials with Vicat softening temperature of 205 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 23 %, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4 [-] Show Material materials with Dielectric constant, 100Hz of 4 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielectric constant, 1MHz of 3.5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 20 kV/mm Show Material materials with Dielectric strength of 20 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 2.00E+12 Ω·cm Show Material materials with Volume resistivity of 2.00E+12 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 13 g/10min Show Material materials with Melt mass-flow rate of 13 g/10min | ISO 1133 | 240°C/2.16kg | |
Melt volume-flow rate | 12 cm³/10min Show Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.6 % Show Material materials with Shrinkage of 1.6 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.6 % Show Material materials with Shrinkage, transverse of 1.6 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≤70MPa |