Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.6 % Show Material materials with Water absorption of 0.6 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.09 GPa Show Material materials with Elastic modulus of 0.09 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 740 % Show Material materials with Elongation of 740 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.09 GPa Show Material materials with Flexural modulus of 0.09 GPa | ISO 178 | ||
Hardness, Ball Indentation | 23.0 °C | 11 MPa Show Material materials with Hardness, Ball Indentation of 11 MPa | ISO 2039-1 | ||
Hardness, Shore D | 23.0 °C | 45 [-] Show Material materials with Hardness, Shore D of 45 [-] | max., ISO 7619-1 | ||
Poisson's ratio | 23.0 °C | 0.49 [-] Show Material materials with Poisson's ratio of 0.49 [-] | |||
Tear strength | 23.0 °C | 122 kN/m Show Material materials with Tear strength of 122 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 123 kN/m Show Material materials with Tear strength, transverse of 123 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 34 MPa Show Material materials with Tensile strength of 34 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy notched | No Break @ 23,-6,-40°C, ISO 179/1eA | ||||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA | ||||
Impact strength, Izod unnotched | No Break @ 23,-40°C, ISO180/1A |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 2.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 2.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 2.1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | -45 °C Show Material materials with Glass transition temperature of -45 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 50 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 50 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 35 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 35 °C | ISO 75-1/-2 | |||
Melting point | 193 °C Show Material materials with Melting point of 193 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 85 °C Show Material materials with Relative temperature index, electrical of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | 120mil | |||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 155 °C Show Material materials with Vicat softening temperature of 155 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 21 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.8 [-] Show Material materials with Dielectric constant, 100Hz of 4.8 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.5 [-] Show Material materials with Dielectric constant, 1MHz of 4.5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 19 kV/mm Show Material materials with Dielectric strength of 19 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 9.5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9.5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 4.00E+14 Ω/sq Show Material materials with Surface resistivity of 4.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 8.00E+12 Ω·cm Show Material materials with Volume resistivity of 8.00E+12 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 8.5 g/10min Show Material materials with Melt mass-flow rate of 8.5 g/10min | ISO 1133 | 220°C/2.16kg | |
Melt volume-flow rate | 7.5 cm³/10min Show Material materials with Melt volume-flow rate of 7.5 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.2 % Show Material materials with Shrinkage of 1.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Material materials with Shrinkage, transverse of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 225°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |