General
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.17 GPa Show Material materials with Elastic modulus of 0.17 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 600 % Show Material materials with Elongation of 600 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 40 % Show Material materials with Elongation at yield of 40 % | ISO 527-1/-2 | ||
Hardness, Shore D | 23.0 °C | 56 [-] Show Material materials with Hardness, Shore D of 56 [-] | max., ISO 7619-1 | ||
Impact strength, Charpy notched | -40.0 °C | 145 kJ/m² Show Material materials with Impact strength, Charpy notched of 145 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
Poisson's ratio | 23.0 °C | 0.49 [-] Show Material materials with Poisson's ratio of 0.49 [-] | |||
Tensile strength | 23.0 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | ISO 527-1/-2 | ||
Yield strength | 23.0 °C | 14 MPa Show Material materials with Yield strength of 14 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glass transition temperature | -20 °C Show Material materials with Glass transition temperature of -20 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 70 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 70 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Melting point | 201 °C Show Material materials with Melting point of 201 °C | ISO 11357-1/-3 | 18°F/min | |||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 180 °C Show Material materials with Vicat softening temperature of 180 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Oxygen index: 20 %, FMVSS Class: SE - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.8 [-] Show Material materials with Dielectric constant, 100Hz of 4.8 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 1MHz of 4.4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 19 kV/mm Show Material materials with Dielectric strength of 19 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 1MHz of 0.04 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 4.00E+13 Ω·cm Show Material materials with Volume resistivity of 4.00E+13 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 8 g/10min Show Material materials with Melt mass-flow rate of 8 g/10min | ISO 1133 | 220°C/2.16kg | |
Melt volume-flow rate | 7 cm³/10min Show Material materials with Melt volume-flow rate of 7 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.4 % Show Material materials with Shrinkage of 1.4 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.4 % Show Material materials with Shrinkage, transverse of 1.4 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 230°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |