General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.18 g/cm³ Show Material materials with Density of 1.18 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.06 GPa Show Material materials with Elastic modulus of 0.06 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 360 % Show Material materials with Elongation of 360 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.07 GPa Show Material materials with Flexural modulus of 0.07 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 40 [-] Show Material materials with Hardness, Shore D of 40 [-] | max., ISO 7619-1 | ||
Shear modulus | 23.0 °C | 0.02 GPa Show Material materials with Shear modulus of 0.02 GPa | ISO 6721 | ||
Tear strength | 23.0 °C | 86 kN/m Show Material materials with Tear strength of 86 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 96 kN/m Show Material materials with Tear strength, transverse of 96 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 20 MPa Show Material materials with Tensile strength of 20 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy notched | No Break @ 23,-6°C, ISO 179/1eA | ||||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA | ||||
Impact strength, Izod unnotched | No Break @ 23,-40°C, ISO180/1A |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -60 °C Show Material materials with Brittleness temperature of -60 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 2.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.8E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | -35 °C Show Material materials with Glass transition temperature of -35 °C | ISO 11357-1/-2 | 18°F/min | |||
Melting point | 170 °C Show Material materials with Melting point of 170 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 90 °C Show Material materials with Relative temperature index, electrical of 90 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2050 J/(kg·K) Show Material materials with Specific heat capacity of 2050 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 115 °C Show Material materials with Vicat softening temperature of 115 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 51 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100Hz | 23.0 °C | 5.7 [-] Show Material materials with Dielectric constant, 100Hz of 5.7 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 5 [-] Show Material materials with Dielectric constant, 1MHz of 5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.06 [-] Show Material materials with Dissipation factor, 100Hz of 0.06 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.05 [-] Show Material materials with Dissipation factor, 1MHz of 0.05 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 2.00E+13 Ω/sq Show Material materials with Surface resistivity of 2.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 4.00E+11 Ω·cm Show Material materials with Volume resistivity of 4.00E+11 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 5.3 g/10min Show Material materials with Melt mass-flow rate of 5.3 g/10min | ISO 1133 | 190°C/2.16kg | |
Melt volume-flow rate | 5 cm³/10min Show Material materials with Melt volume-flow rate of 5 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.8 % Show Material materials with Shrinkage of 0.8 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 0.8 % Show Material materials with Shrinkage, transverse of 0.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 200°C, Min. melt temperature: 190°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 40°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |