Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.15 g/cm³ Show Material materials with Density of 1.15 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.09 GPa Show Material materials with Elastic modulus of 0.09 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 300 % Show Material materials with Elongation of 300 % | min. | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.09 GPa Show Material materials with Flexural modulus of 0.09 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 45 [-] Show Material materials with Hardness, Shore D of 45 [-] | max., ISO 7619-1 | ||
Impact strength, Charpy notched | -40.0 °C | 119 kJ/m² Show Material materials with Impact strength, Charpy notched of 119 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
Tear strength | 23.0 °C | 117 kN/m Show Material materials with Tear strength of 117 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 119 kN/m Show Material materials with Tear strength, transverse of 119 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | ISO 527-1/-2 | ||
Impact strength, Izod unnotched | No Break @23,-40°C, ISO 180/1A |
Thermal
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |
Glass transition temperature | -45 °C Show Material materials with Glass transition temperature of -45 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 57 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 57 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |
Melting point | 204 °C Show Material materials with Melting point of 204 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat softening temperature | 164 °C Show Material materials with Vicat softening temperature of 164 °C | ISO 306 | 90°F, 2 lbf | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 0.4 g/10min Show Material materials with Melt mass-flow rate of 0.4 g/10min | ISO 1133 | 220°C/10kg |
Melt volume-flow rate | 4 cm³/10min Show Material materials with Melt volume-flow rate of 4 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 225°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C |