General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.15 g/cm³ Show Material materials with Density of 1.15 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.1 GPa Show Material materials with Elastic modulus of 0.1 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 202 % Show Material materials with Elongation of 202 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.1 GPa Show Material materials with Flexural modulus of 0.1 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 43 [-] Show Material materials with Hardness, Shore D of 43 [-] | max., ISO 7619-1 | ||
Tear strength | 23.0 °C | 104 kN/m Show Material materials with Tear strength of 104 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 100 kN/m Show Material materials with Tear strength, transverse of 100 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 26 MPa Show Material materials with Tensile strength of 26 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy notched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | -25 °C Show Material materials with Glass transition temperature of -25 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 62 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 62 °C | ISO 75-1/-2 | |
Melting point | 204 °C Show Material materials with Melting point of 204 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat softening temperature | 176 °C Show Material materials with Vicat softening temperature of 176 °C | ISO 306 | 90°F, 2 lbf | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 4.4 g/10min Show Material materials with Melt mass-flow rate of 4.4 g/10min | ISO 1133 | 230°C/10kg | |
Shrinkage | 23.0 °C | 1.7 % Show Material materials with Shrinkage of 1.7 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.6 % Show Material materials with Shrinkage, transverse of 1.6 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C |