Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.15 g/cm³ Show Material materials with Density of 1.15 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.7 % Show Material materials with Water absorption of 0.7 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.06 GPa Show Material materials with Elastic modulus of 0.06 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 510 % Show Material materials with Elongation of 510 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.09 GPa Show Material materials with Flexural modulus of 0.09 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 44 [-] Show Material materials with Hardness, Shore D of 44 [-] | max., ISO 7619-1 | ||
Tear strength | 23.0 °C | 110 kN/m Show Material materials with Tear strength of 110 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 120 kN/m Show Material materials with Tear strength, transverse of 120 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 32 MPa Show Material materials with Tensile strength of 32 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy notched | No Break @ 23,-6,-40°C, ISO 179/1eA | ||||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA | ||||
Impact strength, Izod unnotched | No Break @ 23,-40°C, ISO180/1A | ||||
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |||
Coefficient of thermal expansion | 23.0 °C | 2.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 2.1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | -45 °C Show Material materials with Glass transition temperature of -45 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 58 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 58 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 44 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 44 °C | ISO 75-1/-2 | |||
Melting point | 194 °C Show Material materials with Melting point of 194 °C | ISO 11357-1/-3 | 18°F/min | |||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 155 °C Show Material materials with Vicat softening temperature of 155 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | Oxygen index: 21 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.9 [-] Show Material materials with Dielectric constant, 100Hz of 4.9 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.6 [-] Show Material materials with Dielectric constant, 1MHz of 4.6 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 19 kV/mm Show Material materials with Dielectric strength of 19 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 4.00E+13 Ω·cm Show Material materials with Volume resistivity of 4.00E+13 Ω·cm | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 2.1 g/10min Show Material materials with Melt mass-flow rate of 2.1 g/10min | ISO 1133 | 230°C/2.16kg | |
Melt volume-flow rate | 1.9 cm³/10min Show Material materials with Melt volume-flow rate of 1.9 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.6 % Show Material materials with Shrinkage of 1.6 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.4 % Show Material materials with Shrinkage, transverse of 1.4 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | Carbon Black | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 225°C, Min. melt temperature: 220°C, Max. melt temperature: 240°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C | |