Hytrel® HTR8206

Alternative and trade names
TPC-ET
Want to keep this datasheet? Save it now in your required format

Description

Hytrel® HTR8206 is a High Performance Polyester Elastomer with High Moisture Vapor Transmission Rate Developed for Extrusion and Injection Molding

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Material materials with Density of 1.19 g/cm³

ISO 1183

Water absorption

23.0 °C

35 %

Show Material materials with Water absorption of 35 %

Sim. to ISO 62 | Immersion 24h

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.08 GPa

Show Material materials with Elastic modulus of 0.08 GPa

ISO 527-1/-2

Elongation

23.0 °C

420 %

Show Material materials with Elongation of 420 %

ISO 527-1/-2

Flexural modulus

23.0 °C

0.08 GPa

Show Material materials with Flexural modulus of 0.08 GPa

ISO 178

Hardness, Shore D

23.0 °C

40 [-]

Show Material materials with Hardness, Shore D of 40 [-]

max., ISO 7619-1

Poisson's ratio

23.0 °C

0.49 [-]

Show Material materials with Poisson's ratio of 0.49 [-]

Tensile strength

23.0 °C

20 MPa

Show Material materials with Tensile strength of 20 MPa

ISO 527-1/-2

Impact strength, Charpy notched

No Break @ 23,-6°C, ISO 179/1eA

Impact strength, Charpy unnotched

No Break @ 23,-6°C, ISO 179/1eA

Thermal

PropertyTemperatureValueComment

Melting point

200 °C

Show Material materials with Melting point of 200 °C

ISO 11357-1/-3 | 18°F/min

Specific heat capacity

23.0 °C

2100 J/(kg·K)

Show Material materials with Specific heat capacity of 2100 J/(kg·K)

of melt

Thermal diffusivity

23.0 °C

0 mm²/s

Show Material materials with Thermal diffusivity of 0 mm²/s

Vicat softening temperature

153 °C

Show Material materials with Vicat softening temperature of 153 °C

ISO 306 | 90°F, 2 lbf

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

14 cm³/10min

Show Material materials with Melt volume-flow rate of 14 cm³/10min

ISO 1133

Shrinkage

23.0 °C

1.4 %

Show Material materials with Shrinkage of 1.4 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.5 %

Show Material materials with Shrinkage, transverse of 1.5 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 230°C, Min. melt temperature: 220°C, Max. melt temperature: 240°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C