General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.5 % Show Material materials with Water absorption of 0.5 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.08 GPa Show Material materials with Elastic modulus of 0.08 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 390 % Show Material materials with Elongation of 390 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.08 GPa Show Material materials with Flexural modulus of 0.08 GPa | ISO 178 | ||
Hardness, Shore D | 23.0 °C | 40 [-] Show Material materials with Hardness, Shore D of 40 [-] | max., ISO 7619-1 | ||
Tear strength | 23.0 °C | 110 kN/m Show Material materials with Tear strength of 110 kN/m | ISO 34-1 | ||
Tear strength, transverse | 23.0 °C | 120 kN/m Show Material materials with Tear strength, transverse of 120 kN/m | ISO 34-1 | ||
Tensile strength | 23.0 °C | 29 MPa Show Material materials with Tensile strength of 29 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy notched | No Break @23,-40°C, ISO 179/1A |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.8E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.7E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.7E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | -45 °C Show Material materials with Glass transition temperature of -45 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 59 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 59 °C | ISO 75-1/-2 | |||
Melting point | 208 °C Show Material materials with Melting point of 208 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat softening temperature | 157 °C Show Material materials with Vicat softening temperature of 157 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 0.9 g/10min Show Material materials with Melt mass-flow rate of 0.9 g/10min | ISO 1133 | 230°C/2.16kg |
Melt volume-flow rate | 1 cm³/10min Show Material materials with Melt volume-flow rate of 1 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C |