General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.23 g/cm³ Show Material materials with Density of 1.23 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 0.45 GPa Show Material materials with Elastic modulus of 0.45 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 150 % Show Material materials with Elongation of 150 % | ISO 527-1/-2 |
Hardness, Shore D | 23.0 °C | 58 [-] Show Material materials with Hardness, Shore D of 58 [-] | max., ISO 7619-1 |
Impact strength, Charpy notched | -40.0 °C | 1 kJ/m² Show Material materials with Impact strength, Charpy notched of 1 kJ/m² | ISO 179/1eA |
-6.0 °C | 2.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 2.5 kJ/m² | ISO 179/1eA | |
Poisson's ratio | 23.0 °C | 0.47 [-] Show Material materials with Poisson's ratio of 0.47 [-] | |
Tensile strength | 23.0 °C | 11 MPa Show Material materials with Tensile strength of 11 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | -30 °C Show Material materials with Glass transition temperature of -30 °C | ISO 11357-1/-2 | 18°F/min | |
Melting point | 200 °C Show Material materials with Melting point of 200 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat softening temperature | 163 °C Show Material materials with Vicat softening temperature of 163 °C | ISO 306 | 90°F, 2 lbf | |
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 49 %, Glow Wire Ignition Temperature, 80mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 17.5 kV/mm Show Material materials with Dielectric strength of 17.5 kV/mm | ASTM D 149 | Short Time, 3.2mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 12 g/10min Show Material materials with Melt mass-flow rate of 12 g/10min | ISO 1133 | 220°C/2.16kg | |
Shrinkage | 23.0 °C | 1.2 % Show Material materials with Shrinkage of 1.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.2 % Show Material materials with Shrinkage, transverse of 1.2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Min. melt temperature: 220°C, Max. melt temperature: 240°C |