General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 700 % Show Material materials with Elongation of 700 % | ISO 527-1/-2 |
Hardness, Shore A | 23.0 °C | 62 [-] Show Material materials with Hardness, Shore A of 62 [-] | ISO 7619-1 | 3 seconds |
Tear strength | 23.0 °C | 25 kN/m Show Material materials with Tear strength of 25 kN/m | ISO 34-1 |
Tensile strength | 23.0 °C | 6 MPa Show Material materials with Tensile strength of 6 MPa | ISO 527-1/-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Material materials with Melt mass-flow rate of 18 g/10min | ISO 1133 | 230°C/2.16kg | |
Shrinkage | 23.0 °C | 1 % Show Material materials with Shrinkage of 1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 95°C, Drying Time, Dehumidified Dryer: 4-6h, Melt Temperature Optimum: 190°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 10°C, Max. mold temperature: 50°C, Hold pressure range: as low as possible, Back pressure: 1.5MPa |